1100 Aluminium Round Bar
1100 Aluminium Round Bar is commercially pure aluminum, 99% min pure. Aluminium 1100 H14 Bar is also soft, ductile, and has excellent workability which makes it ideal for projects requiring challenging forming operations. It work-hardens slowly, and is not heat-treatable. Aluminium Flat Bar 1100 has excellent corrosion resistance and weldability, and is most often used in the food processing and chemical industries. Al 1100 Round Bar is noted for having the highest thermal conductivity of any aluminum, and is also known for its high electrical conductivity.
Sasa Aluminium Incorporation is the leading manufacturer and exporter of 1100 Aluminium Round Bar. Supplier of ASTM B221 1100 Aluminium Round Bar in Tempers manufactured in accordance with international standards ASTM B221, ASME SB 221, EN573, and EN485, check 1100 Aluminium Round Bar price. Wholesale Trader of 1100 Commercial Aluminium Bar offered by Sasa Aluminium , China. Stockist of 1100 Aluminium Rod, H32 1100 Aluminium Hex Bar, H38 Commercial 1100 Aluminium Flat Bar, ASME SB221 1100 Aluminium Square Bar, 1100 Mill Finish, 1100 Aluminium Half Round Bar, 1100 Cold Finished Round Bar and 1100 Aluminium Cold Drawn Round Bar in China.
| Specifications of 1100 Aluminium Round Bar: |
| Aluminium Alloy | ASTM B221 1100 |
| Standard | ASTM, ASME, AMS, ASTM B221M, GB/T 3191, JIS H4040, ASTM B221, AMS QQ-A-200/9 |
| Aluminium 1100 Round Bar Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 1100 Bar Form | 1100 Aluminium Square, Round, Hex, Flat, Half Round, Oval, Angle, Rectangular, Wire in Black & Bright Finish |
| Aluminium 1100 Round Bar | Diameter:0.1-600mm,etc |
| Aluminium 1100 Hexagonal Bar | Diameter:0.1-600mm,etc |
| Aluminium 1100 Angle Bar | Size:0.5mm*40mm*40mm-20mm*400mm*400mm |
| Aluminium 1100 Flat Bar | Thickness:0.1-600mm,etc Width:1-2500mm,etc |
| Aluminium 1100 Square Bar | Size:1mm*1mm-800mm*800mm, etc |
| Aluminium 1100 Round Bar Length | 1-12m, Random, Fix & Cut Length or as per clients’ requirement |
| Aluminium 1100 Bar | Bright, Polish & Black |
| Aluminium 1100 Bars Surface | Anodized, Polished, hair line, brush, Mill finished, Bright finish, paper interleaved |
| Aluminium 1100 Solid Round Bar Delivery Time | 10-30 days after receiving the prepayment |
| Aluminium 1100 Round Bar Packaging Details | Export standard package: bundled wooden box, suit for all kinds of transport or be required. |
| ASTM B221 Alloy 1100 Round Bar Outer packing | Export standard, wooden pallet |
| We Export Aluminium 1100 Round Bar to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| Types of 1100 Aluminium Round Bar Manufacturer in China: |
1100 Aluminium Threaded Rods stockholder in China, 1100 Aluminium Forged Round Bars wholesaler in China, Aluminium EN AW 1100 Cold Finish Round Bar importers in China, 1100 Aluminium Hexagonal Rods Cut To Size At Best Price
Standard Dimensions of 1100 Aluminium Round Bar
|
|
Aluminium 1100 Round Bar Manufacturers, Cold Drawn 1100 Aluminium Bar, Cold Forming 1100 Aluminium Material Rod, Cold Rolled 1100 Aluminium Round Rod, 1100 Aluminum Alloy Hollow Bar, UNS A96082 Round Bar Manufacturer in China, EN 485-2 1100 Aluminium Bars & Rods stockist, 1100 Aluminium Round Bar Price in China
| Standard Specification of 1100 Aluminium Round Bar: |
| European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
|---|---|---|---|---|---|---|
| EN AW-1100 | IC | 1100 | Al-99.0 | Al-99.0 | 19000 | 2 S |
The following specifications cover Aluminum 1100
- AMS 4003
- AMS 7220
- ASME SFA5.10 (ER1100)
- ASME SFA5.3 (E1100)
- ASTM B209
- ASTM B210
- ASTM B211
- ASTM B221
- ASTM B241
- ASTM B247
- ASTM B313
- ASTM B316
- ASTM B361
- ASTM B479
- ASTM B483
- ASTM B491
- ASTM B547
- ASTM B548
- AWS A5.10 (ER1100)
- AWS A5.3 (E1100)
- MIL A-52174
- MIL A-52177
- MIL C-26094
- MIL E15597 (MIL-1100)
- MIL I-23413 (MIL-1100)
- MIL R-5674
- MIL S-24149/5
- MIL W-6712
- MIL W-85
- QQ A-1876
- QQ A-225/1
- QQ A-250/1
- QQ A-430
- QQ WW-T-700/1
- SAE J454
- UNS J91100
| 1100 Aluminium Round Bar Weight Chart: |
| Product | Diameter | Weight |
|---|---|---|
| 1100 Aluminium Round Bar | 6 mm | 0,076 Kg/m |
| 1100 Aluminium Round Bar | 7 mm | 0,104 Kg/m |
| 1100 Aluminium Round Bar | 8 mm | 0,136 Kg/m |
| 1100 Aluminium Round Bar | 9 mm | 0,172 Kg/m |
| 1100 Aluminium Round Bar | 9,5 mm | 0,191 Kg/m |
| 1100 Aluminium Round Bar | 10 mm | 0,212 Kg/m |
| 1100 Aluminium Round Bar | 11 mm | 0,257 Kg/m |
| 1100 Aluminium Round Bar | 12 mm | 0,305 Kg/m |
| 1100 Aluminium Round Bar | 12,5 mm | 0,331 Kg/m |
| 1100 Aluminium Round Bar | 13 mm | 0,358 Kg/m |
| 1100 Aluminium Round Bar | 14 mm | 0,416 Kg/m |
| 1100 Aluminium Round Bar | 16 mm | 0,543 Kg/m |
| 1100 Aluminium Round Bar | 16,5 mm | 0,577 Kg/m |
| 1100 Aluminium Round Bar | 18 mm | 0,687 Kg/m |
| 1100 Aluminium Round Bar | 19 mm | 0,766 Kg/m |
| 1100 Aluminium Round Bar | 20 mm | 0,848 Kg/m |
| 1100 Aluminium Round Bar | 22 mm | 1,026 Kg/m |
| 1100 Aluminium Round Bar | 25 mm | 1,325 Kg/m |
| 1100 Aluminium Round Bar | 28 mm | 1,663 Kg/m |
| 1100 Aluminium Round Bar | 30 mm | 1,909 Kg/m |
| 1100 Aluminium Round Bar | 31 mm | 2,038 Kg/m |
| 1100 Aluminium Round Bar | 32 mm | 2,171 Kg/m |
| 1100 Aluminium Round Bar | 35 mm | 2,598 Kg/m |
| 1100 Aluminium Round Bar | 38 mm | 3,062 Kg/m |
| 1100 Aluminium Round Bar | 40 mm | 3,393 Kg/m |
| 1100 Aluminium Round Bar | 45 mm | 4,294 Kg/m |
| 1100 Aluminium Round Bar | 50 mm | 5,301 Kg/m |
| 1100 Aluminium Round Bar | 55 mm | 6,415 Kg/m |
| 1100 Aluminium Round Bar | 60 mm | 7,634 Kg/m |
| 1100 Aluminium Round Bar | 65 mm | 8,959 Kg/m |
| 1100 Aluminium Round Bar | 70 mm | 10,391 Kg/m |
| 1100 Aluminium Round Bar | 75 mm | 11,928 Kg/m |
| 1100 Aluminium Round Bar | 80 mm | 13,572 Kg/m |
| 1100 Aluminium Round Bar | 90 mm | 17,177 Kg/m |
| 1100 Aluminium Round Bar | 100 mm | 21,206 Kg/m |
| 1100 Aluminium Round Bar | 105 mm | 23,379 Kg/m |
| 1100 Aluminium Round Bar | 110 mm | 25,659 Kg/m |
| 1100 Aluminium Round Bar | 120 mm | 30,536 Kg/m |
| 1100 Aluminium Round Bar | 127 mm | 34,203 Kg/m |
| 1100 Aluminium Round Bar | 130 mm | 35,838 Kg/m |
| 1100 Aluminium Round Bar | 140 mm | 41,563 Kg/m |
| 1100 Aluminium Round Bar | 150 mm | 47,713 Kg/m |
| 1100 Aluminium Round Bar | 180 mm | 68,707 Kg/m |
| 1100 Aluminium Round Bar | 200 mm | 84,823 Kg/m |
Theorical Weights Table
The values presented on this table are theorical and they should be confirmed if you make an order.
| 1100 Aluminium Square Bar Weight Chart: |
| Product | Side | Weight |
|---|---|---|
| Aluminium Square Bar | 10 mm | 0,270 Kg/m |
| Aluminium Square Bar | 15 mm | 0,608 Kg/m |
| Aluminium Square Bar | 16 mm | 0,691 Kg/m |
| Aluminium Square Bar | 20 mm | 1,080 Kg/m |
| Aluminium Square Bar | 25 mm | 1,688 Kg/m |
| Aluminium Square Bar | 35 mm | 3,308 Kg/m |
| Aluminium Square Bar | 45 mm | 5,468 Kg/m |
| Aluminium Square Bar | 60 mm | 9,720 Kg/m |
| Aluminium Square Bar | 100 mm | 27,000 Kg/m |
| 1100 Aluminium Rectangular Bar Weight Chart: |
| Product | Width | Thickness | Weight | |
|---|---|---|---|---|
| 1100 Aluminium Rectangular Bar | 20 mm | x | 2 mm | 0,108 Kg/m |
| 1100 Aluminium Rectangular Bar | 15 mm | x | 3 mm | 0,122 Kg/m |
| 1100 Aluminium Rectangular Bar | 20 mm | x | 3 mm | 0,162 Kg/m |
| 1100 Aluminium Rectangular Bar | 25 mm | x | 3 mm | 0,203 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 3 mm | 0,243 Kg/m |
| 1100 Aluminium Rectangular Bar | 40 mm | x | 3 mm | 0,324 Kg/m |
| 1100 Aluminium Rectangular Bar | 15 mm | x | 4 mm | 0,162 Kg/m |
| 1100 Aluminium Rectangular Bar | 20 mm | x | 4 mm | 0,216 Kg/m |
| 1100 Aluminium Rectangular Bar | 25 mm | x | 4 mm | 0,270 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 4 mm | 0,324 Kg/m |
| 1100 Aluminium Rectangular Bar | 15 mm | x | 5 mm | 0,203 Kg/m |
| 1100 Aluminium Rectangular Bar | 20 mm | x | 5 mm | 0,270 Kg/m |
| 1100 Aluminium Rectangular Bar | 25 mm | x | 5 mm | 0,338 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 5 mm | 0,405 Kg/m |
| 1100 Aluminium Rectangular Bar | 40 mm | x | 5 mm | 0,540 Kg/m |
| 1100 Aluminium Rectangular Bar | 50 mm | x | 5 mm | 0,675 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 6 mm | 0,486 Kg/m |
| 1100 Aluminium Rectangular Bar | 40 mm | x | 6 mm | 0,648 Kg/m |
| 1100 Aluminium Rectangular Bar | 60 mm | x | 6 mm | 0,972 Kg/m |
| 1100 Aluminium Rectangular Bar | 20 mm | x | 8 mm | 0,432 Kg/m |
| 1100 Aluminium Rectangular Bar | 25 mm | x | 8 mm | 0,540 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 8 mm | 0,648 Kg/m |
| 1100 Aluminium Rectangular Bar | 40 mm | x | 8 mm | 0,864 Kg/m |
| 1100 Aluminium Rectangular Bar | 50 mm | x | 8 mm | 1,080 Kg/m |
| 1100 Aluminium Rectangular Bar | 55 mm | x | 8 mm | 1,188 Kg/m |
| 1100 Aluminium Rectangular Bar | 60 mm | x | 8 mm | 1,296 Kg/m |
| 1100 Aluminium Rectangular Bar | 80 mm | x | 8 mm | 1,728 Kg/m |
| 1100 Aluminium Rectangular Bar | 100 mm | x | 8 mm | 2,160 Kg/m |
| 1100 Aluminium Rectangular Bar | 20 mm | x | 10 mm | 0,540 Kg/m |
| 1100 Aluminium Rectangular Bar | 25 mm | x | 10 mm | 0,675 Kg/m |
| 1100 Aluminium Rectangular Bar | 30 mm | x | 10 mm | 0,810 Kg/m |
| 1100 Aluminium Rectangular Bar | 40 mm | x | 10 mm | 1,080 Kg/m |
| 1100 Aluminium Rectangular Bar | 50 mm | x | 10 mm | 1,350 Kg/m |
| 1100 Aluminium Rectangular Bar | 60 mm | x | 10 mm | 1,620 Kg/m |
| 1100 Aluminium Rectangular Bar | 80 mm | x | 10 mm | 2,160 Kg/m |
| 1100 Aluminium Rectangular Bar | 100 mm | x | 10 mm | 2,700 Kg/m |
| 1100 Aluminium Rectangular Bar | 200 mm | x | 20 mm | 10,800 Kg/m |
| 1100 Aluminium Round Bar Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| 1 C | 19000 | 1100 | — | 0.1 | — | — | — | 0.50 | 0.6 | — | 0.1 | 0.1 | Aluminum 99.5% Min. | ||
| Aluminium 1100 Round Bar Mechanical Properties: |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) | ||
| EN AW-1100 | O | 75 | 110 | – | – | 25 |
| Alloy Designation | UK Specifications |
US Specifications |
US Federal Specifications |
European Specifications |
Other |
|---|---|---|---|---|---|
| 1100 A91100 |
AMS 4001 1100-0 AMS 4003 1100-H14 AMS 4062 1100-H14 AMS 4102 1100-F Bars, Rods AMS 4180 1100-H18 |
QQ-A-225/1 1100-TF Bar QQ-A-250/1 1100-T0 QQ-A-250/1 1100-H14 WW-T-700/1 1100-H14 MIL-W-6712 Type II |
Aluminum Alloy Heat Treatment Temper Designations for Round Bars
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 1100 Round Rods
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 1100 Bars
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
Application of 1100 Aluminium Rod/ Round Bar
1100 Aluminium Round Bar is the most widely used form of Industrial Aluminium. 1100 Aluminium Rods find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.