2014 T6 Aluminium Sheet
Machinability of aluminium 2014A Sheet is very good. 2014 aluminum sheet is usually used in some occasions with high strength and hardness (including heat). For example, heavy forgings, plate and extrusion materials are used for aircraft structures, the first stage fuel tank of multistage rocket and spacecraft parts, wheels, truck frame and suspension parts.
| Standard Dimensions of 2014 T6 Aluminium Sheet: |
| Alloy | ASTM B209 1050, 1060, 1100, 1235, 3003, 3004, 3105, 5052, 5754, 6061, 8011 |
| Aluminium 2014 T6 Sheet Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 2014 T6 Sheet Thickness | 0.5mm-150mm |
| Aluminium 2014 T6 Sheet Width | 500-2000mm |
| Aluminium 2014 T6 Sheet Length | to clients’ requirement |
| Aluminium 2014 T6 Sheet Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 2014 T6 Aluminium Sheet Coating finish | PVDF, POLYESTER(PE) |
| Surface | Bright, polished, hair line, brush, sand blast, checkered, embossed, etching, etc. |
| Gloss | Meet the customer requirement |
| Total coating thickness | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Coating hardness | (pencil hardness) more than 2H |
| Coating adhesive | No lower than1st grade |
| Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Flexibility (T-bend) | 2T |
| MEK resistance | More than 10 |
| Available Aluminium 2014 T6 Sheet Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 2014 T6 Sheet Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 2014 T6 Sheet Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 2014 T6 Sheet. One 40GP container can load about 24 tons Aluminium 2014 T6 Sheet |
| ASTM B209 Alloy 2014 T6 Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 2014 T6 Sheet is coated with protective polyester material, thickness more than 6 micron | |
| Export to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| 2014 T6 Aluminium Sheet Products Show: |
| 2014 T6 Aluminium Sheets Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| A1050, A1060, A1070, A1100 | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| A3003, A3105, A3004 | 0.2-5.0 | 20-2200 | 20-8000 | O, H14, H18, H24 |
| A5052, A5005, A5083, A5086, A5754 | 0.2-5.0 | 20-2200 | 20-8000 | O, H18, H24, H32, H34, H111, H112 |
| A6061, A6082, A6063 | 0.2-5.0 | 20-2200 | 20-8000 | T4, T6, T651 |
| A8011 | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| Standard Specification of 2014 T6 Aluminium Sheet |
| Specification | Alloy | Temper | Company |
|---|---|---|---|
| Europe | |||
| EN 2089/2395 | 2014A | T6(T62)/T4(T42) | |
| EN 2087/2088 | 2014A clad | T6(T62)/T4(T42) | |
| EN 4101 | 2024 | T4 | |
| EN 2090/2091/2703/4001 | 2024 clad cmq | T3/T4/T4(T42)/T351 | |
| EN 3474/3997/3998/3999 | 2024 cmq | T81/T3/T4(T42)/T351 | |
| EN 2694/EN 3341 | 6061 | T6(T62)/T4(T42) | |
| EN 4449/4450 | 7050 | T76/F(T762) | |
| EN 2696 | 7075 | T6(T62) | |
| EN 2092 | 7075 clad | T6(T62) | |
| EN 2802/3333 | 7475 | T761/F(T762) | |
| EN 2803/3332 | 7475 clad | T761/F(T762) | |
| France | |||
| AIR 9048.010/.030/ | 2014 | F(T42)/F(T62)/T4/ | |
| .020/.040/.050 | 2014 | T6/T451 | |
| AIR 9048.060/.080/.070/.090 | 2014 clad | F(T42)/F(T62)/T4/T6 | |
| AIR 9048.100/.110/.120 | 2024 | ||
| AIR 9048.130/.140 | 2024 clad | F(T42)/T3 | |
| AIR 9048.150 | 2618A | H28(T62) | |
| AIR 9048.170 | 2618A clad | H28(T62) | |
| AIR 9048.190/.200 | 5086 | O, H111/H22, H32 | |
| AIR 9048.210/.220/.230/.240 | 6061 | O, H111(T42)/T4/ O, H111(T62)/T6 | |
| AIR 9048.260/.270 | 7075 | T6/T76 | |
| AIR 9048.280 | 7075 clad | T6 | |
| AIR 9048.290 | 7475 | T76 | Boeing |
| Germany | |||
| W.-Nr. 3.1254 | 2014A | T4, T6 | |
| W.-Nr. 3.1354 | 2024 | O(T42), T3 | |
| W.-Nr. 3.1364 | 2024 clad | O(T42), T3 | |
| W.-Nr. 3.3214 | 6061 | O(T62), T6 | |
| W.-Nr. 3.4364 | 7075 | T6 | |
| W.-Nr. 3.4374 | 7075 clad | O(T62), T6 | |
| W.-Nr. 3.4377 | 7475 clad | T76 | |
| UK | |||
| BS L16/17 | 1200 | H4/O | |
| BS L156/157/158*/159* | 2014A | ||
| 158*/159* | 2014A clad | (T42)(T62) | BAE Systems |
| BS L163/164/165 | 2014A clad | T3/F(T42), T4/T6 | |
| BS L166*/167* | 2014A clad | F(T42), T4/T6 | |
| BS L109/110 | 2024 clad | T3/F(T42) | |
| DTD5070 | 2618A clad | T6 | |
| BS L59/60/61 | 3103 | H6/H2/O | |
| BS L80/81 | 5251 | O/H6 | |
| BS L113 | 6082 | T4, T6 | |
| BS L88 | 7075 clad | T6 | |
| USA | |||
| AMS QQ-A-250/3 | 2014 clad | O, T4, T6 | |
| AMS QQ-A-250/4 | 2024 | O, T3 | |
| AMS 4037 | 2024 | T3 | |
| AMS QQ-A-250/5 | 2024 clad | O, T3 | |
| AMS 4041 | 2024 clad | T3 | |
| AMS QQ-A-250/30 | 2219 | O(T62), T31(T81), T37(T87) | |
| AMS QQ-A-250/2 | 3003 | O, H14 | |
| AMS 4347 | 6013 | T4 | |
| AMS 4216 | 6013 | T6 | |
| AMS 4025/4026/4027 | 6061 | O, F, T4, T42, T45, T6, T62, T651 | |
| AMS QQ-A-250/12 | 7075 | O, T6, T73 | |
| AMS QQ-A-250/24 | 7075 | T76 | |
| AMS QQ-A-250/13 | 7075 clad | O, T6, T73 | |
| AMS QQ-A-250/26 | 7075 clad with 7011 | T76 | |
| AMS QQ-A-250/25 | 7075 clad with 7072 | T76 | |
| European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
|---|---|---|---|---|---|---|
| EN AW-1050 A | 1E | 1050 | Al99.5 | Al99.5 | 19500, 19501 | 1 S |
| EN AW-1070 A | – | 1070 | Al-99.7 | Al-99.7 | 19700 | – |
| EN AW-1100 | IC | 1100 | Al-99.0 | Al-99.0 | 19000 | 2 S |
| EN AW-2011 | FC1 | 2011 | AlCuBiPb | AlCu6BiPb | – | 28S |
| EN AW-2014 | HE15 | 2014 | AlCuSiMn | AlCu4SiMg | 24345 | B26S |
| EN AW-2024 | – | 2024 | AlCuMg2 | AlCu4Mg1 | – | 24 S |
| EN AW-3003 | N3 | 3003 | AlMnCu | AlMn1Cu | 31000 | 3 S |
| EN AW-3103 | – | 3103 | – | AlMn1 | – | – |
| EN AW-6101A | E91E | 6101 | E AlMgSi 0.5 | E AlMgSi(A) | 63401 | D50S |
| EN AW-6005 | – | 6005 | AlMgSi0.7 | AlSiMg | 62400 | C51S |
| EN AW-6351 | HE30 | 6351 | AlMgSi1 | AlSiMg0.5Mn | 64430 | B51S |
| EN AW-6060 | – | 6060 | AlMgSi 0.5 | AlMgSi | – | – |
| EN AW-6061 | HE20 | 6061 | AlMgSiCu | AlMg1SiCu | 65032 | 65S |
| EN AW-6063 | HE9 | 6063 | AlMgSi0.5 | AlMg0.7Si | 63400 | 50S |
| EN AW-6082 | HE30 | 6351 | AlMgSi1 | AlSi1MgMn | 64430 | B51S |
| 2014 T6 Aluminium Sheet Sizes: |
| Sizes (mm) | Theoretical Mass KG/sheet |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
| 2014 T6 Aluminium Sheet Weight Chart: |
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 2014 T6 Aluminium Sheet | 0,30 mm | 0,810 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,40 mm | 1,080 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,50 mm | 1,350 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,60 mm | 1,620 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,70 mm | 1,890 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,80 mm | 2,160 Kg/m2 |
| 2014 T6 Aluminium Sheet | 0,90 mm | 2,430 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,00 mm | 2,700 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,20 mm | 3,240 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,40 mm | 3,780 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,50 mm | 4,050 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,60 mm | 4,320 Kg/m2 |
| 2014 T6 Aluminium Sheet | 1,80 mm | 4,860 Kg/m2 |
| 2014 T6 Aluminium Sheet | 2,00 mm | 5,400 Kg/m2 |
| 2014 T6 Aluminium Sheet | 2,20 mm | 5,940 Kg/m2 |
| 2014 T6 Aluminium Sheet | 2,50 mm | 6,750 Kg/m2 |
| 2014 T6 Aluminium Sheet | 3,00 mm | 8,100 Kg/m2 |
| 2014 T6 Aluminium Sheet | 4,00 mm | 10,800 Kg/m2 |
| 2014 T6 Aluminium Sheet | 5,00 mm | 13,500 Kg/m2 |
| 2014 T6 Aluminium Sheet | 6,00 mm | 16,200 Kg/m2 |
| 2014 T6 Aluminium Sheet | 10,00 mm | 27,000 Kg/m2 |
| 2014 T6 Aluminium Sheet | 12,00 mm | 32,400 Kg/m2 |
| 2014 T6 Aluminium Sheet | 15,00 mm | 40,500 Kg/m2 |
| 2014 T6 Aluminium Sheet | 20,00 mm | 54,000 Kg/m2 |
| 2014 T6 Aluminium Sheet Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| H 15 | 24345 | 2014 | 3.8 | 5.0 | 0.2 | 0.8 | 0.5 | 1.2 | 0.7 | 0.3 | 1.2 | 0.5 | — | ||
| Aluminium 2014 T6 Sheet Mechanical Properties: |
| Alloy | Temper | UTS (Mpa) | Yield Strength (Mpa) | Elongation (%) | ||
|---|---|---|---|---|---|---|
| Minimum | Maximum | Minimum | Maximum | A 50mm (Minimum) | ||
| EN AW-2014 | O | – | 250 | – | 135 | 10 |
| T4 | 370 | – | 230 | – | 11 | |
| T6 | 415 | – | 370 | – | 5 | |
| Alloy Designation | UK Specifications |
US Specifications |
US Federal Specifications |
European Specifications |
Other |
|---|---|---|---|---|---|
| 2014A A92014 |
BS 7 L37 2014A Rivet stock BS 3 L63 2014A-T6 tube BS 2 L77 2014A Forging stock BS 2 L87 2014A-T6 Bar BS 2 L93 2014A-T651 Plate BS L102 2014A-T4 Bar BS L103 2014A-T4 Forging Stock BS L105 2014A-T4 Drawn tube BS L156 2014A-T4 Bare Sheet BS L157 2014A-T6 Bare Sheet BS L158 2014A-T4 Bare Sheet, close tolerance BS L159 2014A-T6 Bare Sheet, close toleranceBS L163 2014A-T3 Clad Sheet BS L164 2014A-T4 Clad Sheet BS L165 2014A-T6 Clad Sheet BS L166 2014A-T4 Clad Sheet, close tolerance BS L167 2014A-T6 Clad Sheet, close toleranceBS L168 2014A-T6 / T6511 BarDTD 5010 Plate DTD 5030 Clad plate DTD 5040 Clad plate BS H15, HS15, HP15, HT15, HE15 |
AMS 4028 2014-T0 Sheet /Plate AMS 4029 2014-T651 Sheet , plate AMS 4121 2014-T6/T6511 Bar AMS 4133 2014-T6 Forging AMS 4134 2014-T6 Die Forging AMS 4153 2014-T6 Extrusions |
QQ-A-200/2 2014-T4 Extruded bar QQ-A-200/2 2014-T6 Extruded bar QQ-A-225/4 2014-T4 Cold finished bar QQ-A-225/4 2014-T6 Cold finished bar QQ-A-250/3 2014-T4 Clad sheet QQ-A-250/3 2014-T6 Clad sheet QQ-A-367 MIL-A-21180 |
WS 3.1255 EN 2087 2014A-T6 Clad sheet EN 2088 2014A-T4 Clad sheet EN 2089 2014A-T6 Sheet EN 2100 2014A-T4511 Extruded bar EN 2324 2014A-T6 EN 2384 2014A-T6511 Extruded bar EN 2395 2014A-T4 Sheet EN 2634 2014A-T4511 Extruded bar EN 2635 2014A-T6511 Extruded bar, peripheral coarse grain control EN 2639 2014A-T6 |
A-U4SG AlCu4SiMg AECMA 2387 |
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
2014 T6 Packing Information of Aluminum plate :
Application of 2014 T6 Aluminium Sheet
2014 T6 Aluminium Sheet is the most widely used form of Industrial Aluminium. 2014 T6 Aluminium Sheets find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.
2014 T6 Aluminium Sheet Applications