5052 Aluminium Plate
Aluminum 5052 Plate in H32 temper has very good corrosion resistance to seawater and marine and industrial atmosphere. 5052 Aluminum Plate also has very good weldability and good cold formability. Aluminum Plate 5052 is a medium to high strength alloy with a strength slightly higher than 5251 and a medium to high fatigue strength.
| Standard Dimensions of 5052 Aluminium Plate: |
| Aluminium Alloy | ASTM B209 5052 |
| Aluminium 5052 Plate Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 5052 Plate Thickness | 0.5mm-150mm |
| Aluminium 5052 Plate Width | 500-2000mm |
| Aluminium 5052 Plate Length | to clients’ requirement |
| Aluminium 5052 Plate Coating | Polyester, Fluorocarbon, polyurethane and epoxy coating |
| 5052 Aluminium Plate Coating finish | PVDF, POLYESTER(PE) |
| Aluminium 5052 Plate Surface | Polished, hair line, brush, sand blast, checkered, embossed, etching, etc. Mill finish, Bright finish, paper interleaved, one side film, both sides film. |
| Aluminium 5052 Plate Gloss | Meet the customer requirement |
| Total coating thickness of Aluminium 5052 Plate | PVDF coating: More than 25 micron; Polyester coating: More than 18 micron |
| Aluminium 5052 Plate Coating hardness | (pencil hardness) more than 2H |
| Aluminium 5052 Plate Coating adhesive | No lower than1st grade |
| Aluminium 5052 Plate Impact resistance | No cracking or peeling (50kg/cm, ASTMD-2794: 1993) |
| Aluminium 5052 Plate Flexibility (T-bend) | 2T |
| Aluminium 5052 Plate MEK resistance | More than 10 |
| Available Aluminium 5052 Plate Stock Sizes | 1ft x 1ft, 1ft x 2ft, 1ft x 4ft, 2ft x 2ft, 2ft x 4ft, 4ft x 4ft, 4ft x 8ft, 4ft x 10ft or Cut to Size or Custom Shape. |
| Aluminium 5052 Plate Delivery Time | 30-60 days after receiving the prepayment |
| Aluminium 5052 Plate Packaging Details | Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 5052 Plate. One 40GP container can load about 24 tons Aluminium 5052 Plate |
| ASTM B209 Alloy 5052 Plate Outer packing | Export standard, wooden pallet |
| Bottom side Aluminium 5052 Plate is coated with protective polyester material, thickness more than 6 micron | |
| We Export Aluminium 5052 Plate to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| AUTHORIZED DISTRIBUTORS OF , NALCO, , THYSSENKRUPP, VIRGO, MANKASIA AND METENERE | |
| Types of 5052 Aluminium Plate Manufacturer in China: |
| 5052 Aluminium Plates Product Range | ||||
|---|---|---|---|---|
| Alloy No. | Thickness (mm) |
Width (mm) |
Length (mm) |
Temper |
| 5052 Aluminium Plate | 0.2-5.0 | 20-2200 | 20-8000 | O, H12, H22, H14, H16, H18, H24, H26 |
| Standard Specification of 5052 Aluminium Plate: |
| China |
U.S.A. |
BRITAIN |
CANADA | GERMANY |
RUSSIA |
I.S.O. |
FRENCH | |
|---|---|---|---|---|---|---|---|---|
| New IS | Old IS | (A.A.) |
(B.S.) |
(DIN) | – | – | – | |
| 52000 | N4 | 5052 | N4 | M57S | Al-Mg.2 | A-Mg | A-Mg-4 | – |
| 5052 Aluminium Plate Sizes: |
| Sizes (mm) | Theoretical Mass KG/Plate |
|---|---|
| 2000 X 1000 X 0.5 | 2500 X 1250 X 0.5 |
| 2000 X 1000 X 0.7 | 2500 X 1250 X 0.7 |
| 2000 X 1000 X 0.9 | 2500 X 1250 X 0.9 |
| 2000 X 1000 X 1.2 | 2500 X 1250 X 1.2 |
| 3000 X 1500 X 1.2 | 2000 X 1000 X 1.6 |
| 2500 X 1250 X 1.6 | 3000 X 1500 X 1.6 |
| 2000 X 1000 X 2.0 | 2500 X 1250 X 2.0 |
| 3000 X 1500 X 2.0 | 2500 X 1250 X 2.5 |
| 2.79 | 4.36 |
| 3.91 | 6.10 |
| 5.02 | 7.85 |
| 6.74 | 10.46 |
| 15.01 | 8.93 |
| 13.95 | 20.09 |
| 11.16 | 17.44 |
| 25.11 | 21.80 |
| 5052 Aluminium Plate Weight Chart: |
Width: 1.000 mm | Length: 2.000 mm
| Product | Thickness | Weight |
|---|---|---|
| 5052 Aluminium Plate | 0,30 mm | 0,810 Kg/m2 |
| 5052 Aluminium Plate | 0,40 mm | 1,080 Kg/m2 |
| 5052 Aluminium Plate | 0,50 mm | 1,350 Kg/m2 |
| 5052 Aluminium Plate | 0,60 mm | 1,620 Kg/m2 |
| 5052 Aluminium Plate | 0,70 mm | 1,890 Kg/m2 |
| 5052 Aluminium Plate | 0,80 mm | 2,160 Kg/m2 |
| 5052 Aluminium Plate | 0,90 mm | 2,430 Kg/m2 |
| 5052 Aluminium Plate | 1,00 mm | 2,700 Kg/m2 |
| 5052 Aluminium Plate | 1,20 mm | 3,240 Kg/m2 |
| 5052 Aluminium Plate | 1,40 mm | 3,780 Kg/m2 |
| 5052 Aluminium Plate | 1,50 mm | 4,050 Kg/m2 |
| 5052 Aluminium Plate | 1,60 mm | 4,320 Kg/m2 |
| 5052 Aluminium Plate | 1,80 mm | 4,860 Kg/m2 |
| 5052 Aluminium Plate | 2,00 mm | 5,400 Kg/m2 |
| 5052 Aluminium Plate | 2,20 mm | 5,940 Kg/m2 |
| 5052 Aluminium Plate | 2,50 mm | 6,750 Kg/m2 |
| 5052 Aluminium Plate | 3,00 mm | 8,100 Kg/m2 |
| 5052 Aluminium Plate | 4,00 mm | 10,800 Kg/m2 |
| 5052 Aluminium Plate | 5,00 mm | 13,500 Kg/m2 |
| 5052 Aluminium Plate | 6,00 mm | 16,200 Kg/m2 |
| 5052 Aluminium Plate | 10,00 mm | 27,000 Kg/m2 |
| 5052 Aluminium Plate | 12,00 mm | 32,400 Kg/m2 |
| 5052 Aluminium Plate | 15,00 mm | 40,500 Kg/m2 |
| 5052 Aluminium Plate | 20,00 mm | 54,000 Kg/m2 |
| 5052 Aluminium Plate Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| N 4 | 52000 | 5052 | — | 0.1 | 1.7 | 2.6 | — | 0.6 | 0.5 | — | 0.5 | 0.4 | Cr+Mn=0.5 | ||
Aluminum Alloy Heat Treatment Temper Designations
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 5052 Plates
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 5052 Plates
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
Application of 5052 Aluminium Plate
5052 Aluminium Plate is the most widely used form of Industrial Aluminium. 5052 Aluminium Plates find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.