63400 Aluminium Round Bar
63400 (UNS A96063) Flat Bar is an aluminum bar also known as 6063 Aluminum Bar that offers good extrudability and high quality surface. 63400 Aluminium Round Bar is used for standard architectural shapes, custom solids and heatsinks. Aluminium Flat Bar 63400 also used for electrical applications in T5, T52 & T6 due to its electrical conductivity.
Aluminium 63400 Bar is commonly referred to as an architectural alloy. It has a high resistance to corrosion with excellent finishing characteristics. IS 63400 Flat Bar has average machinability and forming hot or cold is acceptable. Also due to its conductivity it is utilized in electrical substations. Commonly used in the manufacture of pipe railings, furniture, windows, stair rails, and in pipe railing.
Sasa Aluminium Incorporation is the leading manufacturer and exporter of 63400 Aluminium Round Bar. Supplier of ASTM B221 63400 Aluminium Round Bar in Tempers manufactured in accordance with international standards ASTM B221, ASME SB 221, EN573, and EN485, check 63400 Aluminium Round Bar price. Wholesale Trader of 63400 Commercial Aluminium Bar offered by Sasa Aluminium , China. Stockist of 63400 Aluminium Rod, H32 63400 Aluminium Hex Bar, H38 Commercial 63400 Aluminium Flat Bar, ASME SB221 63400 Aluminium Square Bar, 63400 Mill Finish, 63400 Aluminium Half Round Bar, 63400 Cold Finished Round Bar and 63400 Aluminium Cold Drawn Round Bar in China.
| Specifications of 63400 Aluminium Round Bar: |
| Aluminium Alloy | ASTM B221 63400 |
| Standard | ASTM, ASME, AMS, ASTM B221M, GB/T 3191, JIS H4040, ASTM B221, AMS QQ-A-200/9 |
| Aluminium 63400 Round Bar Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium 63400 Bar Form | 63400 Aluminium Square, Round, Hex, Flat, Half Round, Oval, Angle, Rectangular, Wire in Black & Bright Finish |
| Aluminium 63400 Round Bar | Diameter:0.1-600mm,etc |
| Aluminium 63400 Hexagonal Bar | Diameter:0.1-600mm,etc |
| Aluminium 63400 Angle Bar | Size:0.5mm*40mm*40mm-20mm*400mm*400mm |
| Aluminium 63400 Flat Bar | Thickness:0.1-600mm,etc Width:1-2500mm,etc |
| Aluminium 63400 Square Bar | Size:1mm*1mm-800mm*800mm, etc |
| Aluminium 63400 Round Bar Length | 1-12m, Random, Fix & Cut Length or as per clients’ requirement |
| Aluminium 63400 Bar | Bright, Polish & Black |
| Aluminium 63400 Bars Surface | Anodized, Polished, hair line, brush, Mill finished, Bright finish, paper interleaved |
| Aluminium 63400 Solid Round Bar Delivery Time | 10-30 days after receiving the prepayment |
| Aluminium 63400 Round Bar Packaging Details | Export standard package: bundled wooden box, suit for all kinds of transport or be required. |
| ASTM B221 Alloy 63400 Round Bar Outer packing | Export standard, wooden pallet |
| We Export Aluminium 63400 Round Bar to | Singapore, Indonesia, Ukraine, Korea, Thailand, Vietnam, Saudi Arabia, Brazil, Spain, Canada, USA, Egypt, Iran, China, Kuwait, Dubai, Oman, Kuwait, Peru, Mexico, Iraq, Russia, Malaysia, etc. |
| Types of 63400 Aluminium Round Bar Manufacturer in China: |
63400 Aluminium Threaded Rods stockholder in China, 63400 Aluminium Forged Round Bars wholesaler in China, Aluminium EN AW 63400 Cold Finish Round Bar importers in China, 63400 Aluminium Hexagonal Rods Cut To Size At Best Price
Standard Dimensions of 63400 Aluminium Round Bar
Standard dimensions
|
|
Aluminium 63400 Round Bar Manufacturers, Cold Drawn 63400 Aluminium Bar, Cold Forming 63400 Aluminium Material Rod, Cold Rolled 63400 Aluminium Round Rod, 63400 Aluminum Alloy Hollow Bar, UNS A96082 Round Bar Manufacturer in China, EN 485-2 63400 Aluminium Bars & Rods stockist, 63400 Aluminium Round Bar Price in China
| Standard Specification of 63400 Aluminium Round Bar: |
| European Standard | BS (OLD) | USA (AA) | GERMANY (DIN) | ISO | IS | Canadian |
|---|---|---|---|---|---|---|
| EN AW-6063 | HE9 | 6063 | AlMgSi0.5 | AlMg0.7Si | 63400 | 50S |
| 63400 Aluminium Round Bar Equivalent Grades: |
| China |
U.S.A. |
BRITAIN |
CANADA | GERMANY |
RUSSIA |
I.S.O. |
FRENCH | |
|---|---|---|---|---|---|---|---|---|
| New IS | Old IS | (A.A.) |
(B.S.) |
(DIN) | – | – | – | |
| 63400 | H9 | 6063 | H9 | 50S | Al-Mg-Si 0.5 | – | Al-Si-1 Mg | 6081 |
| 63400 Aluminium Round Bar Weight Chart: |
| Product | Diameter | Weight |
|---|---|---|
| 63400 Aluminium Round Bar | 6 mm | 0,076 Kg/m |
| 63400 Aluminium Round Bar | 7 mm | 0,104 Kg/m |
| 63400 Aluminium Round Bar | 8 mm | 0,136 Kg/m |
| 63400 Aluminium Round Bar | 9 mm | 0,172 Kg/m |
| 63400 Aluminium Round Bar | 9,5 mm | 0,191 Kg/m |
| 63400 Aluminium Round Bar | 10 mm | 0,212 Kg/m |
| 63400 Aluminium Round Bar | 11 mm | 0,257 Kg/m |
| 63400 Aluminium Round Bar | 12 mm | 0,305 Kg/m |
| 63400 Aluminium Round Bar | 12,5 mm | 0,331 Kg/m |
| 63400 Aluminium Round Bar | 13 mm | 0,358 Kg/m |
| 63400 Aluminium Round Bar | 14 mm | 0,416 Kg/m |
| 63400 Aluminium Round Bar | 16 mm | 0,543 Kg/m |
| 63400 Aluminium Round Bar | 16,5 mm | 0,577 Kg/m |
| 63400 Aluminium Round Bar | 18 mm | 0,687 Kg/m |
| 63400 Aluminium Round Bar | 19 mm | 0,766 Kg/m |
| 63400 Aluminium Round Bar | 20 mm | 0,848 Kg/m |
| 63400 Aluminium Round Bar | 22 mm | 1,026 Kg/m |
| 63400 Aluminium Round Bar | 25 mm | 1,325 Kg/m |
| 63400 Aluminium Round Bar | 28 mm | 1,663 Kg/m |
| 63400 Aluminium Round Bar | 30 mm | 1,909 Kg/m |
| 63400 Aluminium Round Bar | 31 mm | 2,038 Kg/m |
| 63400 Aluminium Round Bar | 32 mm | 2,171 Kg/m |
| 63400 Aluminium Round Bar | 35 mm | 2,598 Kg/m |
| 63400 Aluminium Round Bar | 38 mm | 3,062 Kg/m |
| 63400 Aluminium Round Bar | 40 mm | 3,393 Kg/m |
| 63400 Aluminium Round Bar | 45 mm | 4,294 Kg/m |
| 63400 Aluminium Round Bar | 50 mm | 5,301 Kg/m |
| 63400 Aluminium Round Bar | 55 mm | 6,415 Kg/m |
| 63400 Aluminium Round Bar | 60 mm | 7,634 Kg/m |
| 63400 Aluminium Round Bar | 65 mm | 8,959 Kg/m |
| 63400 Aluminium Round Bar | 70 mm | 10,391 Kg/m |
| 63400 Aluminium Round Bar | 75 mm | 11,928 Kg/m |
| 63400 Aluminium Round Bar | 80 mm | 13,572 Kg/m |
| 63400 Aluminium Round Bar | 90 mm | 17,177 Kg/m |
| 63400 Aluminium Round Bar | 100 mm | 21,206 Kg/m |
| 63400 Aluminium Round Bar | 105 mm | 23,379 Kg/m |
| 63400 Aluminium Round Bar | 110 mm | 25,659 Kg/m |
| 63400 Aluminium Round Bar | 120 mm | 30,536 Kg/m |
| 63400 Aluminium Round Bar | 127 mm | 34,203 Kg/m |
| 63400 Aluminium Round Bar | 130 mm | 35,838 Kg/m |
| 63400 Aluminium Round Bar | 140 mm | 41,563 Kg/m |
| 63400 Aluminium Round Bar | 150 mm | 47,713 Kg/m |
| 63400 Aluminium Round Bar | 180 mm | 68,707 Kg/m |
| 63400 Aluminium Round Bar | 200 mm | 84,823 Kg/m |
Theorical Weights Table
The values presented on this table are theorical and they should be confirmed if you make an order.
| 63400 Aluminium Square Bar Weight Chart: |
| Product | Side | Weight |
|---|---|---|
| Aluminium Square Bar | 10 mm | 0,270 Kg/m |
| Aluminium Square Bar | 15 mm | 0,608 Kg/m |
| Aluminium Square Bar | 16 mm | 0,691 Kg/m |
| Aluminium Square Bar | 20 mm | 1,080 Kg/m |
| Aluminium Square Bar | 25 mm | 1,688 Kg/m |
| Aluminium Square Bar | 35 mm | 3,308 Kg/m |
| Aluminium Square Bar | 45 mm | 5,468 Kg/m |
| Aluminium Square Bar | 60 mm | 9,720 Kg/m |
| Aluminium Square Bar | 100 mm | 27,000 Kg/m |
| 63400 Aluminium Rectangular Bar Weight Chart: |
| Product | Width | Thickness | Weight | |
|---|---|---|---|---|
| 63400 Aluminium Rectangular Bar | 20 mm | x | 2 mm | 0,108 Kg/m |
| 63400 Aluminium Rectangular Bar | 15 mm | x | 3 mm | 0,122 Kg/m |
| 63400 Aluminium Rectangular Bar | 20 mm | x | 3 mm | 0,162 Kg/m |
| 63400 Aluminium Rectangular Bar | 25 mm | x | 3 mm | 0,203 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 3 mm | 0,243 Kg/m |
| 63400 Aluminium Rectangular Bar | 40 mm | x | 3 mm | 0,324 Kg/m |
| 63400 Aluminium Rectangular Bar | 15 mm | x | 4 mm | 0,162 Kg/m |
| 63400 Aluminium Rectangular Bar | 20 mm | x | 4 mm | 0,216 Kg/m |
| 63400 Aluminium Rectangular Bar | 25 mm | x | 4 mm | 0,270 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 4 mm | 0,324 Kg/m |
| 63400 Aluminium Rectangular Bar | 15 mm | x | 5 mm | 0,203 Kg/m |
| 63400 Aluminium Rectangular Bar | 20 mm | x | 5 mm | 0,270 Kg/m |
| 63400 Aluminium Rectangular Bar | 25 mm | x | 5 mm | 0,338 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 5 mm | 0,405 Kg/m |
| 63400 Aluminium Rectangular Bar | 40 mm | x | 5 mm | 0,540 Kg/m |
| 63400 Aluminium Rectangular Bar | 50 mm | x | 5 mm | 0,675 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 6 mm | 0,486 Kg/m |
| 63400 Aluminium Rectangular Bar | 40 mm | x | 6 mm | 0,648 Kg/m |
| 63400 Aluminium Rectangular Bar | 60 mm | x | 6 mm | 0,972 Kg/m |
| 63400 Aluminium Rectangular Bar | 20 mm | x | 8 mm | 0,432 Kg/m |
| 63400 Aluminium Rectangular Bar | 25 mm | x | 8 mm | 0,540 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 8 mm | 0,648 Kg/m |
| 63400 Aluminium Rectangular Bar | 40 mm | x | 8 mm | 0,864 Kg/m |
| 63400 Aluminium Rectangular Bar | 50 mm | x | 8 mm | 1,080 Kg/m |
| 63400 Aluminium Rectangular Bar | 55 mm | x | 8 mm | 1,188 Kg/m |
| 63400 Aluminium Rectangular Bar | 60 mm | x | 8 mm | 1,296 Kg/m |
| 63400 Aluminium Rectangular Bar | 80 mm | x | 8 mm | 1,728 Kg/m |
| 63400 Aluminium Rectangular Bar | 100 mm | x | 8 mm | 2,160 Kg/m |
| 63400 Aluminium Rectangular Bar | 20 mm | x | 10 mm | 0,540 Kg/m |
| 63400 Aluminium Rectangular Bar | 25 mm | x | 10 mm | 0,675 Kg/m |
| 63400 Aluminium Rectangular Bar | 30 mm | x | 10 mm | 0,810 Kg/m |
| 63400 Aluminium Rectangular Bar | 40 mm | x | 10 mm | 1,080 Kg/m |
| 63400 Aluminium Rectangular Bar | 50 mm | x | 10 mm | 1,350 Kg/m |
| 63400 Aluminium Rectangular Bar | 60 mm | x | 10 mm | 1,620 Kg/m |
| 63400 Aluminium Rectangular Bar | 80 mm | x | 10 mm | 2,160 Kg/m |
| 63400 Aluminium Rectangular Bar | 100 mm | x | 10 mm | 2,700 Kg/m |
| 63400 Aluminium Rectangular Bar | 200 mm | x | 20 mm | 10,800 Kg/m |
| 63400 Aluminium Round Bar Chemical Composition: |
| Alloy (ISS) | Equivalent alloy (A.A) | Copper | Magnesium | Silicon | Iron | Managanese Others* (Total) | Remarks | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Old | New | U.S.A | Min. | Max. | Min. | Max. | Min. | Max. | Min. | Max. | Max | Max. | Aluminum 99.0% Min. | ||
| H 9 | 63400 | 6063 | — | 0.1 | 0.4 | 0.9 | 0.3 | 0.7 | 0.6 | — | 0.3 | 0.4 | — | ||
| Aluminium 63400 Round Bar Mechanical Properties: |
| Mechanical Properties | |||
| Hardness, Brinell | 73 | 73 | AA; Typical; 500 g load; 10 mm ball |
| Hardness, Knoop | 96 | 96 | Converted from Brinell Hardness Value |
| Hardness, Vickers | 83 | 83 | Converted from Brinell Hardness Value |
| Ultimate Tensile Strength | 241 MPa | 35000 psi | AA; Typical |
| Tensile Yield Strength | 214 MPa | 31000 psi | AA; Typical |
| Elongation at Break | 12 % | 12 % | AA; Typical; 1/16 in. (1.6 mm) Thickness |
| Modulus of Elasticity | 68.9 GPa | 10000 ksi | AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. |
| Ultimate Bearing Strength | 434 MPa | 62900 psi | Edge distance/pin diameter = 2.0 |
| Bearing Yield Strength | 276 MPa | 40000 psi | Edge distance/pin diameter = 2.0 |
| Poisson’s Ratio | 0.33 | 0.33 | |
| Fatigue Strength | 68.9 MPa | 10000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen |
| Machinability | 50 % | 50 % | 0-100 Scale of Aluminum Alloys |
| Shear Modulus | 25.8 GPa | 3740 ksi | |
| Shear Strength | 152 MPa | 22000 psi | AA; Typical |
| Alloy Designation | UK Specifications |
US Specifications |
US Federal Specifications |
European Specifications |
Other |
|---|---|---|---|---|---|
| 6063 | BS H9 Alloy 6063 DTD 372B 6063 |
AMS 4156 6063-T6 Extrusions | QQ-A-200/9 6063 MIL-P-25995 ASTM B210 ASTM B221 ASTM B241 ASTM B345 ASTM B429 ASTM B483 ASTM B491 |
Aluminum Alloy Heat Treatment Temper Designations for Round Bars
Basic Aluminum Heat Treatment Designations
- F As Fabricated
- O Annealed
- H Strain Hardened
- W Solution Heat Treated
- T Solution Heat Treated
Heat Treating T Temper Codes for Aluminium 63400 Round Rods
- T1 – Cooled from an elevated temperature shaping process and naturally aged to a substantially stable condition.
- T2 – Cooled from an elevated temperature shaping process, cold worked, and naturally aged to a substantially stable condition.
- T3 – Solution heat treated, cold worked, and naturally aged to a substantially stable condition.
- T4 – Solution heat treated, and naturally aged to a substantially stable condition.
- T5 – Cooled from an elevated temperature shaping process then artificially aged.
- T6 – Solution heat treated then artificially aged.
- T7 – Solution heat treated then overaged/stabilized.
- T8 – Solution heat treated, cold worked, then artificially aged.
- T9 – Solution heat treated, artificially aged, then cold worked.
- T10 – Cooled from an elevated temperature shaping process, cold worked, then artificially aged.
Additional digits may be used after the first T temper digit to indicate subsequent stress relieving by processes such as stretching, compressing, or a combination.
H Temper Strain Hardening Codes for Aluminium 63400 Bars
- H1 – Strain hardened only
- H2 – Strain hardened and partially annealed
- H3 – Strain hardened and stabilized
- H4 – Strain hardened and lacquered or painted. This assumes that thermal affects from the coating process affect the strain hardening; seldom encountered.
Application of 63400 Aluminium Rod/ Round Bar
63400 Aluminium Round Bar is the most widely used form of Industrial Aluminium. 63400 Aluminium Rods find applications in various industries such as manufacturing cans and packages, transportation, home appliances, building and construction.